LINCOLN AROSTA 304L RVS-laselektrode 4,0 mm 4,4 kg (83 stuks)

The LINCOLN AROSTA 304L is a premium rutile-basic coated stainless steel electrode designed for welding austenitic stainless steels. This electrode offers excellent arc stability, low spatter, and a fine ripple appearance, making it ideal for high-quality welds in demanding applications. With a diameter of 4.0 mm and a package weight of 4.4 kg containing 83 pieces, it is suitable for both professional and industrial use.

Advantages

Excellent arc stability and low spatter ensure clean, efficient welding. Self-releasing slag reduces post-weld cleaning time. The electrode provides good corrosion resistance and high mechanical properties, including tensile strength >520 MPa and impact strength >47 J at -120°C. Suitable for all welding positions and compatible with AC and DC+ current.

Suitable for

• Chemical, food, pharmaceutical, and brewery industries
• General fabrication of stainless steel structures
• Welding of 304L and similar austenitic stainless steels

Key specifications

• Electrode Type: SMAW (Shielded Metal Arc Welding)
• Alloy Grade: 304L (Low Carbon)
• AWS Classification: E308L-17
• EN ISO Classification: EN ISO 3581-A E 19 9 L R 32
• Diameter: 4.0 mm
• Package Weight: 4.4 kg
• Quantity: 83 pieces
• Coating: Rutile-Basic
• Welding Current: AC / DC+
• Welding Positions: All positions (PA, PB, PC, PD, PE, PF)
• Current Range: 100 - 160 A
• Tensile Strength: >520 MPa
• Yield Strength: >320 MPa
• Elongation: >35%
• Impact Strength: >47 J at -120°C
• Approvals: TÜV, CE

Recommendations

For optimal results, use with appropriate welding parameters and ensure proper storage to maintain electrode quality. Preheating is generally not required for 304L. Suitable for use in both workshop and field applications.