Polymaker Panchroma PLA Dual Silk Banquet Gold-Magenta 1,75 mm 1 kg filament

3D printing with standard PLA often leaves visible layer lines and a dull surface, making models look unfinished. The Polymaker Panchroma PLA Dual Silk Banquet Gold-Magenta filament solves this by combining a silky, lustrous finish with a dual-colour effect that shifts between gold and magenta depending on the viewing angle. This iridescent, colour-shifting filament adds depth and visual interest to any print without the need for post-processing.

Who is it for

This filament is ideal for makers, hobbyists, and professionals who want to create eye-catching decorative items, artistic pieces, or prototypes with a premium look. It works with most FDM 3D printers that accept 1.75 mm filament and can handle PLA temperatures.

Main features

• Dual-colour silk PLA with a banquette gold-magenta colour shift
• Silky smooth, lustrous surface finish that hides layer lines
• Iridescent, colour-shifting effect for unique visual appeal
• 1.75 mm diameter with ±0.02 mm dimensional accuracy
• 1 kg net weight on a cardboard spool
• Low odour during printing

Specifications

• Material: PLA (Polylactic Acid)
• Filament type: Dual colour, silk finish
• Colour: Banquet Gold-Magenta
• Diameter: 1.75 mm
• Net weight: 1 kg
• Series: Panchroma
• Print temperature: 190-220 °C
• Heated bed temperature: 25-60 °C
• Dimensional accuracy: ±0.02 mm
• Density: 1.24 g/cm³
• Tensile strength: 50-60 MPa
• Elongation at break: 5-10%
• Heat deflection temperature: ~55 °C
• Spool material: Cardboard
• Packaging: Vacuum-sealed with desiccant
• Recommended print speed: 40-60 mm/s
• Compatibility: FDM 3D printers

Tips

For the best colour-shifting effect, print models with curved surfaces and multiple angles. Use a nozzle temperature at the lower end of the range to preserve the silk finish. Store the filament in a dry box when not in use to maintain print quality.