BambuLab PETG-CF Malachite Green filament 1,75 mm 1 kg met spoel

BambuLab PETG-CF Malachite Green is a high-performance carbon fiber reinforced PETG filament designed for demanding 3D printing applications. This 1kg spool features a 1.75mm diameter with tight tolerances, delivering exceptional stiffness, strength, and heat resistance. The matte malachite green finish provides a premium aesthetic while the carbon fiber content (~15-20%) enhances dimensional stability and reduces warping.

Advantages

Compared to standard PETG, PETG-CF offers significantly higher tensile and flexural strength, making it ideal for functional parts. The carbon fiber reinforcement minimizes shrinkage (0.4-0.6%) and improves layer adhesion. It prints smoothly at speeds up to 150 mm/s with a hardened steel nozzle (0.4mm or larger). The spool is made from ABS plastic, ensuring durability during storage and use.

Suitable for

• Functional prototypes and end-use parts
• Tools, fixtures, and jigs
• Structural components requiring high stiffness
• Automotive and industrial applications
• Enclosures and brackets

Key specifications

• Material: PETG-CF (Polyethylene Terephthalate Glycol - Carbon Fiber)
• Color: Malachite Green
• Net Filament Weight: 1 kg
• Filament Diameter: 1.75 mm
• Diameter Tolerance: ±0.03 mm
• Recommended Printing Temperature: 250-270 °C
• Recommended Bed Temperature: 70-90 °C (with glue stick)
• Recommended Print Speed: 30-150 mm/s
• Carbon Fiber Content: ~15-20%
• Nozzle Compatibility: Hardened Steel, 0.4mm or larger
• Spool Material: ABS Plastic
• Tensile Strength (X/Y): 45 ± 4 MPa
• Flexural Strength (X/Y): 80 ± 5 MPa
• Impact Strength (X/Y, Izod): 8 ± 0.5 kJ/m²
• Heat Deflection Temperature (HDT @ 0.45 MPa): 70 °C
• Density: 1.23 g/cm³
• Shrinkage Rate: 0.4-0.6%
• Moisture Sensitivity: Moderate

Recommendations

For best results, use a hardened steel nozzle and ensure the filament is stored in a dry environment. A glue stick on the build plate is recommended for adhesion. This filament is not suitable for brass nozzles due to abrasiveness.