ESAB OK 61.30 E316L-17 rutielbeklede RVS-elektrode, 3,2 mm x 350 mm, 1,7 kg pak

Stainless steel welding electrode with rutile coating, delivering smooth arc stability and excellent slag removal for high-quality welds on austenitic stainless steels. The ESAB OK 61.30 is a 3.2 mm diameter electrode, 350 mm long, supplied in a 1.7 kg pack. It is classified as E316L-17 per AWS and EN ISO 3581-A E 19 12 3 L R 12, suitable for AC and DC+ currents in all positions except vertical down.

Advantages

Rutile coating ensures a stable arc, fine droplet transfer, and self-releasing slag, minimizing post-weld cleaning. The low carbon content (<0.03%) reduces the risk of intergranular corrosion, while the molybdenum addition improves pitting resistance in chloride environments. The electrode operates with a wide amperage range of 80–120 A, providing versatility for various material thicknesses.

Suitable for

• Welding of 316L, 316Ti, 1.4401, 1.4404, 1.4435, and 1.4571 stainless steels
• Applications requiring high corrosion resistance in chemical, food processing, and marine environments
• All-position welding (PA, PB, PC, PE, PF) except vertical down
• Both AC and DC+ power sources

Key specifications

• AWS Classification: E316L-17
• EN ISO Classification: 3581-A E 19 12 3 L R 12
• Electrode Type: Rutile coated
• Material Type: Austenitic stainless steel
• Welding Current: AC, DC+
• Welding Positions: All positions except vertical down (PA, PB, PC, PE, PF)
• Electrode Diameter: 3.2 mm
• Electrode Length: 350 mm
• Package Weight: 1.7 kg
• Typical Amperage Range (3.2 mm): 80–120 A
• Tensile Strength (Rm): 550–600 MPa
• Yield Strength (Rp0.2): 400–450 MPa
• Elongation (A5): 35–40%
• Impact Strength (CVN @ -120°C): >47 J
• Carbon Content (Weld Metal): <0.03%
• Chromium Content: 18.0–19.0%
• Nickel Content: 11.5–12.5%
• Molybdenum Content: 2.5–3.0%

Recommendations

For optimal results, use DC+ polarity with a short arc and maintain a travel angle of 70–80°. Preheat is not required for thicknesses up to 10 mm; for thicker sections, preheat to 100–150°C. Interpass temperature should not exceed 150°C to preserve corrosion resistance. Store electrodes in a dry place and re-dry at 250–300°C for 2 hours if exposed to moisture.