SUNLU PLA+ Silk Filament 1,75 mm zwart 1 kg

Discover the SUNLU PLA+ Silk Filament, a premium 3D printing material that combines the ease of PLA+ with a stunning silk-like finish. This filament produces glossy, smooth prints with a metallic sheen, perfect for decorative objects, artistic models, and functional prototypes. The 1.75 mm diameter ensures compatibility with most FDM 3D printers, while the tight tolerance of ±0.02 mm guarantees consistent extrusion and high-quality results.

Advantages

Silk PLA+ offers a unique aesthetic appeal with its glossy, smooth surface and metallic sheen, setting your prints apart. It exhibits low warping and low odor, making it suitable for indoor use. The filament is vacuum sealed with desiccant to keep it dry and ready to print. With a wide printing temperature range (200-230 °C) and good tensile strength (50-60 MPa), it delivers reliable performance for both beginners and experienced users.

Suitable for

• Decorative items and art pieces
• Cosplay props and costume accessories
• Prototyping and functional parts
• Gifts and personalized objects
• Educational projects

Key specifications

• Material: PLA+ (Polylactic Acid Plus)
• Finish: Silk (Glossy, Smooth, Metallic-like Sheen)
• Color: Black
• Filament Diameter: 1.75 mm
• Diameter Tolerance: ±0.02 mm
• Net Filament Weight: 1 kg (2.2 lbs)
• Gross Weight (with spool): Approx. 1.25 kg
• Recommended Print Temperature: 200-230 °C
• Recommended Bed Temperature: 50-65 °C (or Off)
• Print Speed: 50-100 mm/s
• Tensile Strength: 50-60 MPa
• Elongation at Break: 20-30%
• Density: 1.24 g/cm³
• Spool Diameter: 200 mm
• Spool Width: 63 mm
• Spool Hub Hole Diameter: 56 mm
• Compatibility: FDM 3D Printers
• Packaging: Vacuum Sealed with Desiccant
• Odor: Low
• Warping: Low

Recommendations

For best results, store the filament in a dry environment and use a filament dryer if necessary. Adjust print temperature within the recommended range based on your printer and desired finish. This filament is ideal for projects where appearance matters, but it may not be suitable for high-stress mechanical parts due to its silk properties.