Polymaker PA07027 PolyTerra PLA Pro filament 1,75 mm 1 kg Army Beige

Polymaker PA07027 PolyTerra PLA Pro combines high stiffness with high impact resistance, offering a balance that standard PLA often lacks. This Army Beige filament prints with a matte finish, giving parts a refined, non-glossy appearance.

Highlights

• High stiffness and impact resistance
• Matte surface finish
• Diameter tolerance ±0.03 mm
• Roundness tolerance ±0.02 mm
• 1 kg net weight spool

In daily use

With a recommended nozzle temperature of 210 °C and bed temperature of 50 °C, this filament is easy to print on most FDM printers. It works well at speeds from 30 to 70 mm/s with the cooling fan on. The material has a density of 1.23 g/cm³, tensile strength of 45 MPa, and elongation at break of 10%, making it suitable for functional prototypes and durable parts.

Full specifications

• Material: PolyTerra PLA Pro
• Filament Diameter: 1.75 mm
• Net Weight: 1 kg
• Colour: Army Beige
• Recommended Nozzle Temperature: 190-230 °C (210 °C recommended)
• Recommended Bed Temperature: 25-60 °C (50 °C recommended)
• Recommended Printing Speed: 30-70 mm/s
• Cooling Fan: On
• Density: 1.23 g/cm³
• Tensile Strength: 45.0 MPa
• Elongation at Break: 10.0 %
• Flexural Modulus: 2000 MPa
• Impact Strength (Charpy Notched): 10.0 kJ/m²
• Diameter Tolerance: ± 0.03 mm
• Roundness Tolerance: ± 0.02 mm
• Glass Transition Temperature (Tg): ~60 °C
• Vicat Softening Temperature (VST): ~60 °C

Final note

PolyTerra PLA Pro is a reliable choice for makers who need parts that can withstand occasional impacts without sacrificing printability.